Shear Bond Strength Comparison of Different Adhesive Systems to Calcium Silicate-based Materials

Hyunok Shin; Kim Mi Sun; NAM OK HYUNG; Lee Hyo-Seol; Chul Choi Sung; KIM， KWANG CHUL

doi:10.5933/JKAPD.2018.45.4.445

The aim of this study was to measure the shear bond strength (SBS) of different adhesive systems to calcium silicatebased materials (Biodentine and RetroMTA). Eighty cylindrical acrylic blocks, with a hole (5.0 mm diameter, 2.0 mm height) in each, were prepared. The holes were filled with Biodentine (BD) and RetroMTA (RMTA), and the specimens were divided into 2 groups. Each group was classified into 4 subgroups: ClearfilTM SE (CSE) ; AQ bond (AQ) ; All bond universal Self-etch (ABU-SE) ; and All bond universal Total-etch (ABU-TE). After the application of different adhesive systems, composite resin (Z350) was applied over BD and RMTA. The SBS was measured using a universal testing machine, and the data were compared using the Kruskal-Wallis test and the Mann-Whitney test. The highest and lowest values of SBS were observed for BD-ABU-SE and RMTA-AQ, respectively. No significant differences were found in the SBS between ABU-TE and ABU-SE and between ABU-TE and CSE to BD and RMTA. According to the data, BD showed a higher SBS than did RMTA when BD and RMTA are compared in the same adhesive agents. Further, among all groups, composite resin with ABU-SE showed better bond strength to BD and RMTA.

Citation status

KCI Citation Counts (0)
REFERENCES (29)
열림/닫힘 버튼
* 2021년 이후 발행 논문의 참고문헌은 현재 구축 중입니다.

[journal] Gulati S / 2014 / Comparison of shear bond strength of resin-modified glass ionomer to conditioned and unconditioned mineral trioxide aggregate surface: An in vitro study / J Conserv Dent 17 : 440~443

[journal] Cantekin K / 2015 / Bond strength of different restorative materials to light-curable mineral trioxide aggregate / J Clin Pediatr Dent 39 : 143~148

[journal] Torabinejad M / 1999 / Clinical applications of mineral trioxide aggregate / J Endod 25 : 197~205

[journal] Antunes Bortoluzzi E / 2006 / The use of a setting accelerator and its effect on pH and calcium ion release of mineral trioxide aggregate and white Portland cement / J Endod 32 : 1194~1197

[journal] Boutsioukis C / 2008 / Ex vivo study of the efficiency of two techniques for the removal of mineral trioxide aggregate used as a root canal filling material / J Endod 34 : 1239~1242

[journal] About I / 2016 / Biodentine: from biochemical and bioactive properties to clinical applications / G Ital Endod 30 : 81~88

[journal] Nowicka A / 2013 / Response of human dental pulp capped with biodentine and mineral trioxide aggregate / J Endod 39 : 743~747

[journal] Cantekin K / 2014 / Evaluation of shear bond strength of two resin-based composites and glass ionomer cement to pure tricalcium silicate-based cement (Biodentine®) / J Appl Oral Sci 22 : 302~306

[journal] Kang CM / 2017 / A randomized controlled trial of various MTA materials for partial pulpotomy in permanent teeth / J Dent 60 : 8~13

[journal] Van Meerbeek B / 2003 / Buonocore memorial lecture. Adhesion to enamel and dentin:current status and future challenges / Oper Dent 28 : 215~235

[journal] 김용일 / 2012 / Microleakage and Microtensile Bond Strength Evaluation of the Various Generations of Dentin Bonding Agents / 대한치과재료학회지 / 대한치과재료학회 39(2) : 119~128

[journal] Subramaniam P / 2009 / Mineral trioxide aggregate as pulp capping agent for primary teeth pulpotomy : 2 year follow up study / J Clin Pediatr Dent 33 : 311~314

[journal] Altunsoy M / 2015 / Shear bond strength of a self-adhering flowable composite and a flowable base composite to mineral trioxide aggregate, calcium-enriched mixture cement, and Biodentine / J Endod 41 : 1691~1695

[journal] Atabek D / 2012 / Bond strength of adhesive systems to mineral trioxide aggregate with different time intervals / J Endod 38 : 1288~1292

[journal] Tunç ES / 2008 / The evaluation of bond strength of a composite and a compomer to white mineral trioxide aggregate with two different bonding systems / J Endod 34 : 603~605

[journal] Davidson CL / 1984 / The competition between the composite-dentin bond strength and the polymerization contraction stress / J Dent Res 63 : 1396~1399

[journal] Deepa VL / 2016 / Shear bond strength evaluation of resin composite bonded to three different liners : TheraCal LC, Biodentine, and resin-modified glass ionomer cement using universal adhesive: An in vitro study / J Conserv Dent 19 : 166~170

[journal] Ha WN / 2015 / D90: the strongest contributor to setting time in mineral trioxide aggregate and Portland cement / J Endod 41 : 1146~1150

[journal] Karadas M / 2016 / Evaluation of the bond strength of different adhesive agents to a resinmodified calcium silicate material (TheraCal LC) / Scanning 38 : 403~411

[journal] Shin JH / 2014 / Effect of mineral trioxide aggregate surface treatments on morphology and bond strength to composite resin / J Endod 40 : 1210~1216

[journal] Yoshida Y / 2004 / Comparative study on adhesive performance of functional monomers / J Dent Res 83 : 454~458

[journal] Gandolfi MG / 2011 / Development of the foremost light-curable calcium-silicate MTA cement as root-end in oral surgery. Chemical–physical properties, bioactivity and biological behavior / Dent Mater 27 : 134~157

[journal] Jang JH / 2016 / Comparative study of the dentin bond strength of a new universal adhesive / Dent Mater J 35 : 606~612

[journal] Bayrak S / 2009 / Shear bond strengths of different adhesive systems to white mineral trioxide aggregate / Dent Mater J 28 : 62~67

[journal] Kayahan MB / 2009 / Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate / Int Endod J 42 : 1004~1014

[journal] Hashem DF / 2014 / The physical characteristics of resin composite–calcium silicate interface as part of a layered/laminate adhesive restoration / Dent Mater 30 : 343~349

[journal] Hanabusa M / 2012 / Bonding effectiveness of a new ‘multi-mode’ adhesive to enamel and dentine / J Dent 40 : 475~484

[journal] Marchesi G / 2014 / Adhesive performance of a multi-mode adhesive system: 1-year in vitro study / J Dent 42 : 603~612

[journal] Ajami AA / 2013 / Comparison of shear bond strength of resin-modified glass ionomer and composite resin to three pulp capping agents / J Dent Res Dent Clin Dent Prospects 7 : 164~168

KJC Korea
Journal Central

Statistics

Tools

Sharing

Issue List

Citation status