2004, Vol.16, No.4

Textile Coloration and Finishing KCI Impact Factor : 0.0

pISSN : 1229-0033 / eISSN : 2234-036X
https://journal.kci.go.kr/ksdf

In recent, development of nano fiber has been one of the most active subjects in the world. Nano fiber is defined as a ultra fine yarn with a diameter unit of 10~100 10-9meter, which is possible to be produced by an electro-spinning technology. In this study, physical characteristics and dyeing properties of nylon 66 nano fiber were investigated. Nylon 66 nano fiber was dyed with levelling type acid dyes. X-ray diffraction method and DSC analysis were used for the measurement of the degree of crystallization. Analysis of amino end groups was also performed in order to examine a relationship between number of amino groups and its dyeing property as well as water absorption behavior. The maximum exhaustion % of dyes and dyeing rate under various dyeing conditions, such as dyeing temperature and pH in dye bath, along with build-up properties for 2 acid dyes were evaluated. It was found that the degree of crystallization of nano fiber was smaller than that of regular fiber, and amino end groups of nano fiber were less than regular fiber. Half dyeing time of nano fiber was shorter than regular fiber because of the bigger specific surface area. Effect of pH on exhaustion % was small in case of nano fiber. Exhaustion of nano fiber increased with higher concentration of dye.

In this work, Aqueous sericin solution was prepared by degumming process with electrolytic reduction water.Then, the microfiltration and ultrafiltration systems were applied to the concentration of aqueous sericin solution. The objective of this study was to select the optimum operating condition among the different pressure. The permeate flux and rejection ratio were observed with time, pressure, flow rate and concentration. and, the wastewater and permeated water quality values such as pH, BOD, COD, and NH levels were measured.In order to see the influence of electrolytic reduction water, the flux of pure water and electrolytic reduction water by PVDF22(MF) and PS100(UF) membrane was measured. In microfiltration system, the relative flux reduction decreased rapidly to 0.02 in the 30min, as the concentration polarization and gel layer formation were increased. and then the sericin concentration rejection ratio was 40%.In ultrafiltration system, the permeate flux decreased with time and concentration, and increased with the operating pressure and flow rate. Optimal condition in PS100 membrane system for sericin concentration was operating pressure 1.464kgf/cm2, operating flow rate 7 /min at 40 . At that time, sericin concentration rejection ratio was 83% respectably. The sericin solution was concentrated from 0.1wt％ solution to 0.2 wt ％ solution during about 2 hrs by the UF filteration membrane system.

Both poly(vinyl alcohol)(PVA)-I2 and PVA-dye polarizing film were prepared using PVA with number-average degree of polymerization of 1,700, 2,300, 2,600. The optical property of used dye in this study closed to the that of iodine. The PVA-dye polarizing film was prepared through the dyeing process. In comparison of the result of the measurement of the heat and humidity resistance of two types polarizing films, it of PVA-dye polarizing film was higher than that of a conventional PVA-I2 polarizing film.The transmittance and the polarization efficiency of PVA-dye polarizing fjlm was significantly influenced by dye concentration, dipping time, salt concentration, and temperature of dye bath. The PVA-dye polarizing film exhibited a high polarization efficiency of 99.3% and a good transmittance of 42.4%.