Methacryloxypropyl trimethoxysilane (MAPTMS), a hybrid organic-inorganic monomer, was photografted onto PET fabric using benzophenone (BP) as a photoinitiator. It was found that a UV energy of 43.2J/cm2 was required to optimally photograft the MAPTMS onto PET fabrics which was applied with an aqueous formulation of 10% MAPTMS, 20% BP and 0.5% N-Methyldiethanol amine (MDEA). The MDEA additive was efficient in reducing atmospheric oxygen inhibition of polymer radicals which eliminated compulsory nitrogen inerting. The surface grafting of PET fabrics was verified by fourier transform infrared spectroscopy (FT-IR) and scanning electron spectroscopy (SEM). The grafted PET fabrics with the hybrid monomer showed higher thermal stability due to the introduced silane component in the monomer as ascertained by higher char content at 800oC, which increased to 14.5% for the 15.8% grafting compared to 8.2% for the untreated.

Flame-retardant cotton fabrics were prepared by UV curing of photocurable aqueous formulations of phosphorous-containing methacrylate monomers and 2-hydroxy-2-methyl-1-phenyl-1-propanone as flame retardants and a photoinitiator respectively, which is an environmentally friendly and energy-saving process. The characterization of the UV-coated cotton fabric was made by ATR, TGA and limited oxygen index measurement. UV cured coating onto cotton fabrics reduced the first thermal decomposition temperature and mass loss as well as increase in the amount of char residue compared with the untreated cotton fabric presumably due to modified thermal decomposition process. The LOI values up to 28.5 and 27.2 were obtained by the UV curing of MMEP and TMEP respectively. The treatment was durable to five laundering cycles, which was more prominent in the case of trifunctional TMEP treatment.

The cotton yarn was subjected to bio-polishing treatment with three commercial enzymes(Cellusoft L, Denimax-991L and Denimax-acid) to remove the fuzz on the cotton yarn. Also, enzyme treated cotton yarns were compared with singeing cotton yarns. Experimental variables of enzyme treated cotton yarn were as follow: concentration of enzyme solution and NaOH, dipping time, and processing temperature. The enzymatic treatments were evaluated by analyzing the effect on yarn count, twist contraction, evenness and tenacity. As the results, enzymatic treatment on cotton yarn induced same effects as the traditional singeing treatment. Also, silket treatment of cotton yarn after bio-polishing enhanced the tensile properties of the cotton yarn.