2006, Vol.18, No.4

Textile Coloration and Finishing KCI Impact Factor : 0.0

pISSN : 1229-0033 / eISSN : 2234-036X
https://journal.kci.go.kr/ksdf

Tannin treatment has been used for improving the color fastness of dyed materials. In natural dyeing, the tannin treatment is highly effective in improving the fastness. The chitosan treatment also improves the fastness and depth of shade in natural dyeing. In this study, the effects of tannin and chitosan pre-treatment on the color and fastness in loess dyeing were investigated. Cotton woven fabric specimens and cotton knit fabric specimens were pre-treated with chitosan solution in acetic acid, and the specimens were then treated with or without tannin. The specimens were finally dyed with loess. The tannin treatment decreased the K/S values, while the chitosan treatment increased the K/S. Both the tannin treatment and the chitosan treatment increased the wash fastness and light fastness. In tannin treatment, tannin component and Fe component of loess may react together to decrease the lightness and develop dark color. For maintaining inherent color of the loess, it is much preferable to employ chitosan treatment rather than tannin treatment.

Black-dyed PET fabrics were sputtered with stainless steel through DC-magnetron type device to investigate the possibility of coloration effect, and then considered the morphological structure and physical characteristics such as water permeation ability and washing fastness. Change in color was estimated on the basis of CIELAB color system. The color coordination of metal plated PET was shifted to yellow-red from red-blue. Colour difference(△E*) was increased by sputtering conditions with increasing ion current and treatment time. Especially, Lightness(L*) value of PET was remarkably increased by sputtering, whereas Chroma(C*) increased gradually. From SEM analysis, rough and uneven craters were found and thickened on the fiber surfaces with longer sputtering time. And washing fastness was a little poor and absorption ability slightly decreased. There were little changes of breaking load and breaking extension. It was evident that observed uneven craters in the plated thin layer resulted in the colour change of PET fabrics by sputtering treatments.

Lyocell is a not only environmentally-friendly but also very advantageous fiber. When Lyocell is soaked in water, its wet tenacity does not decrease and elongation and moisture regain of it are better than cotton. However, one drawback of lyocell is its fibrillation. The fibrills of lyocell were generated during wet process such as scouring and dyeing deteriorates the dyeing color depth and the appearance of fabric.The purpose of this study was to decrease the fibrillation tendency of lyocell fabric using crosslinking agent, epichlorohydrine(ECH). The effects of NaOH scouring and ECH crosslinking were observed. The different types of ECH addition methods to lyocell and the various concentrations of ECH in crosslinking reaction onto dyeing characteristic and fibriallation were investigated. Weight loss and whiteness index of crosslinked lyocell by ECH were examined. K/S values of ECH treated lyocell fabrics dyed with reactive dye were measured and SEM images of untreated and treated lyocells were observed extensively to define the fibrillation tendency. The results were as follows ; 1) ECH treatment showed the effect of weight loss and scouring because ECH crosslinking reaction was conducted in alkaline condition. 2) The increase in ECH concentration from 5 to 30% does not affected K/S value changes. 3) ECH crosslinking can effectively prevent the fibrillation tendency of lyocell.